Our products are highly acknowledged for its features like high resistance to the corrosion, wear and tear, fine finishing, free from casting defects, dimensional accuracy, ultimately providing longer life. We offer our products to the customers at affordable prices. Our products conform to pre-defined industrial standards.
201: This is a yellow pink colour alloy recommended for Handmade Jewellery purpose processing 18-22k. It contains Medium silver contents. Its characteristics leads it to be little bit hard. Melting point is 1060-1090 C.
210: This is a Light Pink colour alloy, recommended for Handmade & Casting Jewellery purpose processing 14-18k. It contains Medium silver contents. Melting point is 1040-1080 C.
206 : This is a yellow pink colour alloy recommended for Handmade Jewellery purpose processing 18-22k. It contains High silver contents. Its characteristics leads it to be little bit hard. Melting point is 1060-1090 C.
104 : This is good red colour alloy which contains very low silver contents. Its softness makes it suitable for all types of processing. It’s melting point is 1050-1090 C.
108 : This is good red colour alloy which contains low silver contents. Its softness makes it suitable for 20-22k for handmade jewellery. It’s melting point is 1050-1090 C.
G-10 : This is good reddies yellow colour alloy which contains Medium silver contents. Its softness makes it suitable for 20-22k for handmade jewellery. It’s melting point is 1050-1090 C.
M-16 : This Alloy is suitable for 08-14K & 20-22K due to Medium silver contents alloy. It is rich yellow in colour. The outcome of M-16 is American Yellow. Melting point is 980-1020 C.
65-M : This Alloy has Good Silver contents which make it suitable for microfusion and all purpose. It is the most common American Yellow Gold Alloy for 14 & 22K. This Alloy is recommended for getting bright and smooth surface which reduces the finishing process. Melting point is 980-1020 C.
D-10 : This alloy is an intensive yellow alloy which recommended for 8-12K. Low silver contents make it cost effective. It can be used for all purpose. Melting point is 990-1020 C.
S-30 : This alloy stands behind the M-94 ALLOY a slight difference between both the alloys are it has more gold tone. Excellent result for wax setting & Handmade Jewellery. It is suitable for 18-22K and melting point is 960-1000 C.
This Alloy is similar to M-92 ALLOY. Because of its yellow colour it is suitable for 18-22K. It gives 100% good result for wax setting & Handmade Jewellery. As it have the characteristics of M-92 so it is recommended for export products. It’s melting point is 980-1020 C.
SP WHITE : This alloy can be used in any type of processing. As it’s very high versatility it is very famous Alloy. It is very suitable for casting purpose, with more than 30% elongation. The main characteristics of this alloy is it gives different shades of white to the metal. For obtaining various colours it can be used in various shades even than the results are good for 14-18K. This alloy is very cost effective. It’s melting point is 1080-1100 C.
S 15 : This alloy is white in colour and due to it’s whiteness it does not require rhodium plating. This alloy contains high nikel. It is recommended for microfision and of 18K and above. Due to silver presence this alloy is soft. Melting point of S 15 is 1100-1140 C.
Palladium is used in high quantity than which makes it suitable for all types of jewellery. The characteristics of palladium makes it white-grey. For getting good white alloy minimum quantity of palladium is used. This is an expensive alloy in comparison with other alloys. Rhodium plating is not necessary. It’s melting point is 1100-1140 C. Annealing at 700 C. After casting give cooling time of 20 - 25 mins. before putting in water.
916-S : 916 Solder Alloy is KDM Free. It is used for handmade Jewellery. This Alloy is very simple to use, just add Fine Gold in Solder Alloy. Process : Add 8.400gm of Alloy in 91.600gm of Fine Gold. Do not mix other Materials.
BRASS : Oxidation free Brass alloy is used in Master. It is suitable for Casting Purpose. It’s cost is very low even then it has the strict production specification. It is recommended for imitation jewellery and is not suitable for Gold jewellery. There is very low variation in its colour in hot climates. It’s melting point is 910-940 C. Annealing at 600 C. After casting give cooling time of 20 - 25 mins. before putting in water.
COPPER : Oxidation free high purity Copper. It’s cost is very low even then it has the strict production specification. There is very low variation in its colour in hot climates. An addition of 25-40% silver in alloy encounters the above drawback & makes it suitable for jewellery. Melting point of COPPER is 1040-1080 C.
S-88 : S-88 is a high quality Brass. It is used in 92½ silver jewellery and also to make Starling Silver. This Alloy is oxidations free, Anti tarnish and gives high finish in Fine Grain Casting. It is used in Master Making. Melting point is 920-960 C.
This alloy is an intensive yellow alloy which recommended for 22K Casting Jewellery. Very low silver contents makes it cost effective. It is used for casting purpose. Melting point is 1000-1040 C.